L Style Inserts
-
P Steel (5)
-
P0Low-Carbon Steels, Long Chipping C < .25%; <125 HB; <530 N/mm^2 UTS (5)
-
P1Low-Carbon Steels, Short Chipping C < .25%; <125 HB; <530 N/mm^2 UTS (5)
-
P2Medium and High Carbon Steels C < .25%; <220 HB; <25 HRC; >530 N/mm^2 UTS (5)
-
P3Alloy Steels & Tool Steels C > .25%; <330 HB; <35 HRC; 600-850 N/mm^2 UTS (5)
-
P4Alloy Steels & Tool Steels C > .25%; 350-420 HB; 35-43 HRC; 850-1400 N/mm^2 UTS (5)
-
P5Ferritic, Martensitic, and PH Stainless Steels <330 HB; <35 HRC; 600-900 N/mm^2 UTS (5)
-
P6High Strength Ferritic, Martensitic, and PH Stainless Steels 350-450 HB; 35-43 HRC; 900-2400 N/mm^2 UTS (5)
-
-
M Stainless Steel (1)
-
M1Austenitic Stainless Steel 130-200 HB; <600 N/mm^2 UTS (1)
-
M2High Strength Austenitic Stainless and Cast Stainless Steels 150-230 HB; <25 HRC; >600 N/mm^2 UTS (1)
-
M3Duplex Stainless Steel 135-275 HB; <30 HRC; 500-1200 N/mm^2 UTS (1)
-
-
K Cast Iron (4)
-
K1Gray Cast Iron 120-290 HB; <32 HRC; 125-500 N/mm^2 UTS (4)
-
K2Low and Medium Strength CGI and Ductile Irons 130-260 HB; <28 HRC; <600 N/mm^2 UTS (4)
-
K3High Strength Ductile and Austempered Ductile Iron 180-350 HB; <43 HRC; >600 N/mm^2 UTS (4)
-
-
US (1)
-
Heavily Interrupted Cut (4)
-
Lightly Interrupted Cut (4)
-
Smooth Cut (4)
-
4.0 (7)
-
8.0 (1)
-
0.095 in (1)
-
0.157 in (7)
-
2.401 mm (1)
-
4.0 mm (7)
-
AT15S (1)
-
TTR (1)
-
WK20CT (4)
-
WP15CT (2)
-
19.05 mm (4)
-
30.0 mm (3)
-
40.0 mm (1)
-
0.75 in (4)
-
1.181 in (3)
-
1.575 in (1)
-
13 (2)
-
16 (1)
-
EN95 (1)
-
T (4)